Stainless Steel Welded Tubes are widely used in industries that demand high resistance to corrosion and heat. Among the many grades, SS 347 (UNS S34700) stands out for its exceptional resistance to intergranular corrosion, especially after exposure to temperatures that result in chromium carbide precipitation (around 800-1500°F or 425-815°C). The addition of niobium (columbium) stabilizes this austenitic steel, making it ideal for high-temperature applications.
For specialized applications, precision dimensions play a critical role. The SS Seamless Tube Grade 347 with a 15.8mm diameter and 1.2mm wall thickness is perfect for industries that require tubes with high mechanical strength, dimensional accuracy, and corrosion resistance.
Due to its excellent properties, SS 347 seamless tubes with a 15.8mm diameter and 1.2mm thickness are suitable for a wide range of applications:
While both seamless and welded tubes are available in SS 347, seamless tubes offer several advantages:
Stainless Steel Pipes Dimension – (S.S. Pipes) | ||||||||||||
Wall thickness in mm. | 0.5 | 0.6 | 0.7 | 0.8 | 1 | 1.2 | 1.6 | 2 | 2.6 | 3 | 3.2 | 3.6 |
---|---|---|---|---|---|---|---|---|---|---|---|---|
O.D. in mm. | Weight in kg/meter | |||||||||||
6 | 0.069 | 0.081 | 0.093 | 0.104 | 0.125 | 0.144 | 0.176 | – | – | – | – | – |
9.52 | 0.112 | 0.134 | 0.154 | 0.174 | 0.213 | 0.249 | 0.317 | – | – | – | – | – |
10 | 0.119 | 0.141 | 0.163 | 0.184 | 0.225 | 0.264 | 0.336 | – | – | – | – | – |
12.7 | 0.153 | 0.182 | 0.21 | 0.238 | 0.293 | 0.345 | 0.444 | – | – | – | – | – |
14 | 0.169 | 0.201 | 0.233 | 0.264 | 0.325 | 0.384 | 0.496 | – | – | – | – | – |
15.87 | 0.192 | 0.229 | 0.266 | 0.301 | 0.372 | 0.44 | 0.571 | 0.694 | – | – | – | – |
19 | 0.231 | 0.276 | 0.32 | 0.364 | 0.45 | 0.534 | 0.696 | 0.85 | 1.066 | 1.2 | 1.264 | – |
25 | 0.306 | 0.366 | 0.425 | 0.484 | 0.6 | 0.714 | 0.936 | 1.15 | 1.456 | 1.65 | 1.744 | 1.926 |
25.4 | 0.311 | 0.372 | 0.432 | 0.492 | 0.61 | 0.726 | 0.952 | 1.17 | 1.482 | 1.68 | 1.776 | 1.962 |
31.8 | – | – | – | – | – | 0.918 | 1.208 | 1.49 | 1.898 | 2.16 | 2.288 | 2.538 |
38 | – | – | – | – | – | 1.104 | 1.456 | 1.8 | 2.301 | 2.625 | 2.784 | 3.096 |
44.5 | – | – | – | – | – | 1.299 | 1.716 | 2.125 | 2.724 | 3.113 | 3.304 | 3.681 |
50.8 | – | – | – | – | – | 1.488 | 1.968 | 2.44 | 3.133 | 3.585 | 3.808 | 4.248 |
63.5 | – | – | – | – | – | – | 2.476 | 3.075 | 3.959 | 4.538 | 4.824 | 5.391 |
76.1 | – | – | – | – | – | – | 2.98 | 3.705 | 4.778 | 5.483 | 5.832 | 6.525 |
101.6 | – | – | – | – | – | – | 4 | 4.98 | 6 | 7 | 7,872 | 8.82 |
CHEMICAL COMPOSITION (IN PERCENTAGE) | ||||||||||
Grade | C (Max) | Mn (Max) | P (Max) | S (Max) | Si (Max) | Cr | Ni | Mo | Nitrogen (Max) | Cu/ Others |
301 | 0.15 | 2 | 0.045 | 0.03 | 1 | 16.00 – 18.00 | 6.00 – 8.00 | – | 0.1 | – |
---|---|---|---|---|---|---|---|---|---|---|
304 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 18.00 – 20.00 | 8.00- 10.50 | – | 0.1 | – |
304L | 0.03 | 2 | 0.045 | 0.03 | 0.75 | 18.00 – 20.00 | 8.00- 12.00 | – | 0.1 | – |
310S | 0.08 | 2 | 0.045 | 0.03 | 1.5 | 24.00- 26.00 | 19.00 – 22.00 | – | – | – |
316 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 16.00 – 18.00 | 10.00 – 14.00 | 2.00 – 3.00 | 0.1 | – |
316L | 0.03 | 2 | 0.045 | 0.03 | 0.75 | 16.00 – 18.00 | 10.00 – 14.00 | 2.00 – 3.00 | 0.1 | – |
317 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 18.00 – 20.00 | 11.00 – 14.00 | 3.00 – 4.00 | 0.1 | – |
317L | 0.03 | 2 | 0.045 | 0.03 | 0.75 | 18.00 – 20.00 | 11.00 – 15.00 | 3.00 – 4.00 | 0.1 | – |
321 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 17.00 – 19.00 | 9.00 – 12.00 | – | 0.1 | Ti5 ( C + N ) Min or 0.70 max |
347 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 17.00 – 19.00 | 9.00 – 13.00 | – | – | Cb= 10x ( C Min ) or 1.00 Max |
409 | 0.08 | 1 | 0.04 | 0.01 | 1 | 10.50 – 11.75 | 0.5 | – | – | Ti= 6x (C+ N ) Min or 0.70 Max |
409M | 0.03 | 0.81.2 | 0.03 | 0.03 | 0.40.75 | 11.00- 12.00 | 1.5 max. | – | – | Ti= 6x (C) Min or 0.70 Max |
410S | 0.08 | 1 | 0.04 | 0.03 | 1 | 11.50- 13.50 | 0.6 | – | – | – |
410 | 0.15 | 1 | 0.04 | 0.03 | 1 | 11.50- 13.50 | 0.75 | – | – | – |
420 | 0.35 | 0.5 | 0.035 | 0.015 | 0.5 | 12.00 – 13.00 | 0.20.3 | – | – | – |
430 | 0.12 | 1 | 0.04 | 0.03 | 1 | 16.00 – 18.00 | 0.75 | – | – | – |
JSL AUS | 0.08 | 7.08.0 | 0.07 | 0.03 | 0.75 | 15.50 – 16.50 | 4.25 – 4.75 | – | – | 0.9 – 1.10 |
JS- 203 | 0.08 | 9.2510.25 | 0.07 | 0.03 | 0.75 | 14.25 – 15.25 | 2.25 – 2.75 | – | – | 1.60- 2.0 |
301M | 0.1 | 4.55.5 | 0.06 | 0.03 | 0.75 | 14.50 – 15.50 | 6.0 – 7.0 | – | – | 1.70- 1.90 |
* Thickness of 1.27mm & below will have elongation of 20% min. |
MECHANICAL PROPERTIES | |||||
Grade | Tensile Strength Mpa, (Min) |
Yield Strength Mpa, (Min) |
%Age Elongation in 50mm gauge length min |
Hardness (Max) | |
BHN | Rb | ||||
301 | 515 | 205 | 40 | 217 | 95 |
---|---|---|---|---|---|
304 | 515 | 205 | 40 | 201 | 92 |
304L | 485 | 170 | 40 | 201 | 92 |
310S | 515 | 205 | 40 | 217 | 95 |
316 | 515 | 205 | 40 | 217 | 95 |
316L | 485 | 170 | 40 | 217 | 95 |
317 | 515 | 205 | 35 | 217 | 95 |
317L | 515 | 205 | 40 | 217 | 95 |
321 | 515 | 205 | 40 | 217 | 95 |
347 | 515 | 205 | 40 | 201 | 92 |
409 | 380 | 170 | 20 | 179 | 88 |
409M | 430 | 275 | 20 | 187 | 90 |
410S | 415 | 205 | 22 | 183 | 89 |
410 | 450 | 205 | 20 | 217 | 89 |
420 | 700( max ) | – | 15 | 217 | 95 |
430 | 450 | 205 | 22 | 183 | 89 |
JSL AUS | 515 | 205 | 40 | 217 | 95 |
JS- 203 | 515 | 205 | 40 | 217 | 95 |
301M | 515 | 205 | 40 | 217 | 95 |